The common pouring methods used in investment casting are:
熔模铸造时常用的浇注方法有：
1) Hot gravity casting
1）热型重力浇注
This is the most widely used form of casting, that is, the shell is removed from the furnace and poured at high temperatures.
这是用得最广泛的一种浇注形式，即型壳从焙烧炉中取出后，在高温下进行由浇注。
At this time, the metal is cooled slowly in the mold shell, and the mold can be filled in the case of high fluidity, so the casting can replicate the shape of the cavity well and improve the accuracy of the casting.
此时金属在型壳中冷却较慢，能在流动性较高的情况下充填铸型，故铸件能很好复制型腔的形状，提高了铸件的精度。
However, the slow cooling of the casting in the hot type will make the grain coarse, which reduces the mechanical properties of the casting.
但铸件在热型中的缓慢冷却会使晶粒粗大，这就降低了铸件的机械性能。
When pouring carbon steel castings, the surface of the castings that cool slowly is also easy to oxidize and decarburize, thereby reducing the surface hardness, finish and dimensional accuracy of the castings.
在浇注碳钢铸件时，冷却较慢的铸件表面还易氧化和脱碳，从而降低了铸件的表面硬度、光洁度和尺寸精度。
2) vacuum suction pouring
2）真空吸气浇注
The mold shell is placed in a vacuum pouring box, and the gas in the mold cavity is absorbed through the tiny pores in the mold shell, so that the liquid metal can better fill the mold cavity, copy the shape of the mold cavity, improve the casting accuracy, and prevent the defects of insufficient porosity and pouring.
将型壳放在真空浇注箱中，通过型壳中的微小孔隙吸走型腔中的气体，使液态金属能更好地充填型腔，复制型腔的形状，提高铸件精度，防止气孔、浇不足的缺陷。
The law has been applied abroad.
该法已在国外应用。